Kingfa JH-R2G10 P60
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ezGBpo_Kingfa-JH-R2G10-P60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa JH-R2G10 P60 is a polycarbonate + acrylonitrile butadiene styrene (PC + ABS) material, and its filler is 10% glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa JH-R2G10 P60 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 76.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3 | 4350 | MPa | ASTM D790 |
| Flexural Strength 4 | 119 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 280 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 130 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 120 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 28 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 245 - 270 | °C | |
| Front Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 80.0 - 130 | °C | |
| Back Pressure | 0.00 - 0.700 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 285°CInjection Speed: 60 to 90% |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8673-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| GAZOLE™ 6200PF | Gharda Chemicals Ltd. | PBI | GAZOLE™ |
| EMOPLEN® A 830 T15 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Kepital® LX-30 BK | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Plaskolite Acrylic PL-30 | Plaskolite, Inc. | Acrylic (PMMA) | Plaskolite Acrylic |