Di-Pak™ R-4545/17
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | exg3K8_Di-Pak-R-4545-17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIGID DI-PAK R-4545 Series A very low viscosity potting and encapsulating system with excellent flow and penetration into the most intricate electronic components, without voids or porosity. The R-4545 Series cure to a hard, shiny, high gloss, plastic finish that is free from "blushing" under all humidity conditions. The R-4545 Series is ideal for electrical applications where surface finish and appearance are critical. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.050 to 0.25 | % | ASTM D2566 |
| Weight - per cubic inch | 18 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 63 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 1.0 | hr | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2530 | MPa | ASTM D638 |
| Tensile Strength | 55.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 66.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 29 | J/m | ASTM D256 |
| Unnotched Izod Impact | 46 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.22 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.3E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.10 | ||
| 100 kHz | 3.80 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.012 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 42, Mix Ratio by Volume: 50 | ||
| Thermoset Mix Viscosity (25°C) | 550 | cP | ASTM D4878 |
| Demold Time (21°C) | 1400 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resalloy™ 165 | Resirene, S.A. de C.V. | Styrene Epoxy Copolymer | Resalloy™ |
| Nipol® 1312LV | Zeon Chemicals L.P. | NBR | Nipol® |
| BC PS MF-303 | BC Chemical Co., Ltd. | PS (HIPS) | BC PS |
| Karina IVORY PVC COMPOUND 807D35/ 1-C-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OnForce™ LFT LF6600-5018 X2 NHFR BLACK | PolyOne Corporation | Nylon 66 | OnForce™ LFT |