Taitacell EPS 321LS
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitacell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ewDDoG_Taitacell-EPS-321LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitacell EPS 321LS is an Expanded Polystyrene material. It is available in Asia Pacific or North America. Important attributes of Taitacell EPS 321LS are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | > 0.0180 | g/cm³ | ASTM D792 |
| Pentane Content | < 5.0 | % | |
| Water Content | < 0.50 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Bead Size 1 | 700.0 to 1100.0 | µm | |
| Chemical Resistance | |||
| Acid | Good | ||
| Alkali | Good | ||
| Solvent | Poor | ||
| Expandability | 25.0 to 70.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | > 0.245 | MPa | ASTM D790 |
| Compressive Strength (10% Strain) | > 0.0785 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | 0.031 to 0.042 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HF-1 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 95% min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAJORIS UG300 - 8229 | AD majoris | Nylon 66 | MAJORIS |
| ResMart Plus Nylon 6 | ResMart | Nylon 6 | ResMart Plus |
| TOTAL Polypropylene PPH 7069 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| YUPLENE® BX3800 | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| Gallonprene® GP210-8002L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |