DOWLEX™ NG 5056.01G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | euB5l9_DOWLEX-NG-5056-01G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™NG 5056.01G polyethylene resin polyethylene resin is a new generation of linear low density polyethylene resin, used for high-quality blown film processing, the processing requires a combination of excellent optical properties, tear strength and heat sealing, and very good toughness/stiffness between the balance. DOWLEX NG5056.01G polyethylene resin has a very low crystal point level, making it very suitable for composite films and other special packaging. This resin contains slip agent and opening agent. Note: When applied to the application field of contact food, DOWLEX NG 5056.01G polyethylene resin should comply with the U.S. Food and Drug Administration when it is unmodified and the processing process follows the requirements of good manufacturing practices. The requirements of the 177.1520 regulations and the requirements of the food contact regulations of most European countries. Please contact your nearest Dow representative for proof of compliance with the Food Contact Act. The purchaser remains responsible for determining whether the use of its products complies with all relevant regulations. Application field:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 1.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 3(vs. Itself - Dynamic) | 0.24 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Energy 4(50 µm) | 3.50 | J | ASTM D5748 |
| Film Puncture Force 5(50 µm) | 54.0 | N | ASTM D5748 |
| Tensile Modulus 6 | ISO 527-3 | ||
| 2% secant, MD : 50 µm | 198 | MPa | ISO 527-3 |
| 2% secant, TD : 50 µm | 238 | MPa | ISO 527-3 |
| Tensile Stress 7 | ISO 527-3 | ||
| MD : Yield, 50 µm | 7.50 | MPa | ISO 527-3 |
| TD : Yield, 50 µm | 8.00 | MPa | ISO 527-3 |
| MD : Break, 50 µm | 38.0 | MPa | ISO 527-3 |
| TD : Break, 50 µm | 37.0 | MPa | ISO 527-3 |
| Tensile Elongation 8 | ISO 527-3 | ||
| MD : Break, 50 µm | 810 | % | ISO 527-3 |
| TD : Break, 50 µm | 920 | % | ISO 527-3 |
| Dart Drop Impact 9(50 µm) | 450 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 10 | ASTM D1922 | ||
| MD : 50 µm | 890 | g | ASTM D1922 |
| TD : 50 µm | 1100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 11 | 104 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 12(45°, 50.0 µm) | 61 | ASTM D2457 | |
| Haze 13(50.0 µm) | 8.9 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 管形薄膜挤出的制造条件： 熔体温度：190 至 240°C。 放大比范围：1.5 至 3:1。 建议的厚度范围：10 至 150 µm。 |
| Note Message | |
|---|---|
| 1 . | Compression molding |
| 2 . | Compression molding |
| 3 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 4 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 5 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 6 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 7 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 8 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 9 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 10 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 11 . | Compression molding |
| 12 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| 13 . | Blow molded film extruded at 235°C, 50 microns, 2.5 BUR, 1.5mm die gap. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide A28 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| AKROTEK® PAEK CF 30 black (5216) | AKRO-PLASTIC GmbH | PEKK | AKROTEK® |
| CERTENE™ LLBF-221D | Muehlstein | LLDPE | CERTENE™ |
| CYCOLAC™ HMG47MD resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| ECONAMID庐 66FLST1 | DOMO Engineering Plastics SPA | Nylon 66 | ECONAMID® |