NILAMID® A3 GB50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | etzyA1_NILAMID-A3-GB50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NILAMID® A3 GB50 is a Polyamide 66 (Nylon 66) compound, 50% glass bead reinforced, heat stabilized. This compound is intended for injection molding. NILAMID® A3 GB50 is primarily designed for the Automotive industry. It is also suitable for Electrical and Electronic or Industrial & Consumer applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.5 | % | |
| Flow : 23°C | 1.5 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.2 | % | |
| Saturation, 23°C | 4.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5650 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 6.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 125 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (3.20 mm, Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E685 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Vexel PBT B12GF30 SA | Custom Resins Group | PBT | Vexel |
| AIE PA66 6010F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Ethylplus 619 LD | Fainplast Compounds S.r.l | LDPE | Ethylplus |
| Hylon® N2025HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |