Hylon® N1040MGHLUV2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Hylon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | etqBuw_Hylon-N1040MGHLUV2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 66, 25% Mineral / 15% Glass Filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 131 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 9100 | MPa | ISO 178 |
| Flexural Stress | 186 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TAIRILAC AG15AB | Formosa Plastics Corporation | ABS | TAIRILAC |
| Sympoxy™ 1010/809 | Hapco Inc. | Epoxy | Sympoxy™ |
| Evermore PUR B-637ND | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| LNP™ LUBRILOY™ D2000P compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |