Jam PE 09X02
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Jam Petrochemical Company |
| Trademark: | Jam PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | etlhtN_Jam-PE-09X02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jam PE 09X02 is a Linear Low Density Polyethylene product. It can be processed by blown film and is available in Africa & Middle East. Applications of Jam PE 09X02 include film and wrap. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.909 to 0.911 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 9.60 | MPa | |
| TD : Yield, 25 µm, Blown Film | 8.80 | MPa | |
| MD : Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 32.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 640 | % | |
| TD : Break, 25 µm, Blown Film | 880 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 320 | g | |
| TD : 25 µm, Blown Film | 80 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 84 | ASTM D1790 | |
| Haze (25.0 µm, Blown Film) | 2.6 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/ABS-G20 | Polymer Resources Ltd. | PC+ABS | PRL |
| Menzolit® BMC 1100 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| NOPLA® KE901 | Kolon Plastics, Inc. | PEN | NOPLA® |
| Dryflex® C1 5065 | ELASTO | TPE | Dryflex® |
| Eptalloy™ PX-057 | Mitsui Chemicals, Inc. | EPDM | Eptalloy™ |