NEONIT® SK61 L5G
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | SBHPP |
| Trademark: | NEONIT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | etiMOI_NEONITSK61L5G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NEONIT® SK61 L5G is a long glass fiber reinforced epoxy molding compound with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited for over molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.15 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.060 | % | ISO 62 |
| Post Shrinkage | -0.020 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18000 | MPa | ISO 527-2 |
| Tensile Stress | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 16000 | MPa | ISO 178 |
| Flexural Stress | 215 | MPa | ISO 178 |
| Compressive Stress | 248 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 51 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 150 | °C | TMA |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.0E-5 | cm/cm/°C | TMA |
| Lateral | 5.3E-5 | cm/cm/°C | TMA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 1040EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| Halene P B202S | Haldia Petrochemicals Ltd. | PP Random Copolymer | Halene P |
| Karina BROWN PVC COMP -E 856-36/639-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| Plaslube® TPX-PA6/6-01072 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Sylvin 9048-60 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |