VENYL UGK306 - 8229
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | esgsXd_VENYL-UGK306---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UGK306 - 8229 is a glass fibre reinforced polyamide 66 (nanotechnologies) with improved electrical properties intended for Injection moulding. APPLICATIONS VENYL UGK306 - 8229 has been developed especially for demanding applications for good resistant final parts and rigidity combined with good electrical conductivity. Products requiring excellent combination between electrical and mechanical properties. VENYL UGK306 - 8229 is only available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.70 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10200 | 10800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | 184 | MPa | ISO 527-2 |
| Flexural Modulus | 9610 | 9400 | MPa | ISO 178 |
| Flexural Stress | 308 | 303 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 50 to 62 | 57 to 61 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 270 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 254 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+6 to 1.0E+7 | -- | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+2 to 1.0E+3 | -- | ohms·cm | DIN 53482 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 295 to 310 | °C | |
| Middle Temperature | 290 to 305 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 90.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 291-60B150 | ExxonMobil Chemical | TPV | Santoprene™ |
| Silmar® SIL93AE-1045 | Interplastic Corporation | Polyester, TS | Silmar® |
| VAMPAMID 66 3026 V0 | Vamp Tech | Nylon 66 | VAMPAMID |
| Geon™ Vinyl Rigid Molding M4605 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| HiFill® ABS GF30 HT | Techmer Engineered Solutions | ABS | HiFill® |