BMC 100
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Bulk Molding Compounds, Inc. |
| Trademark: | BMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | esGEHe_BMC-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BMC 100 is a Thermoset Polyester product. It can be processed by injection molding and is available in North America. Typical application: Electrical/Electronic Applications. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.94 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 40 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 34.5 | MPa | ASTM D638 |
| Flexural Modulus | 13100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 89.6 | MPa | ASTM D790 |
| Compressive Strength | 145 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.8E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Arc Resistance (1.59 mm) | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (1.59 mm) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 32.2 to 43.3 | °C | |
| Middle Temperature | 32.2 to 43.3 | °C | |
| Front Temperature | 32.2 to 43.3 | °C | |
| Mold Temperature | 157 to 177 | °C | |
| Injection Pressure | 6.89 | MPa | |
| Clamp Tonnage | 3.4 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unipren® Elastomers B3 NTLA010 64A UP319 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Celanex® 3300-2LM | Celanese Corporation | PBT | Celanex® |
| Elastron® V V100.A55.N | Elastron USA, Inc. | TPV | Elastron® V |
| EMERGE™ PC 8600-10 | Trinseo | PC | EMERGE™ |
| LONGLITE® PBT 3010-200X | CCP Group | PBT | LONGLITE® PBT |