Order Products : sales@su-jiao.com

HI-ZEX MILLION™ 340M

Category:	HMWPE , High Molecular Weight Polyethylene
Manufacturer:	Mitsui Chemicals, Inc.
Trademark:	HI-ZEX MILLION™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	esFUqL_HIZEXMILLION340M.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

HI-ZEX MILLION™340M is a high molecular weight polyethylene material,. This product is available in the Asia-Pacific region and is processed by extrusion, molding or plunger extrusion.

HI-ZEX MILLION™The main features of 340M are:

Impact resistance

accessible food

moisture resistance

chemical resistance

Wear-resistant

Typical application areas include:

engineering/industrial accessories

food contact applications

medical/health care

bag/lining

sheet

General Information
Features	Impact resistance, high Good wear resistance Low temperature impact resistance Good chemical resistance Compliance of Food Exposure Low or no water absorption Self-lubricating
Uses	Films Lining Gear Conveyor accessories Washer Valve/valve components Non-specific food applications Industrial application Pipe fittings Roller Connector Agricultural application Sheet Sporting goods Fiber Repair Repair Medical/nursing supplies
Agency Ratings	FDA 21 CFR 177.1520(c) 2.2
Processing Method	Extrusion Molding Plunger press-out

Physical	Nominal Value	Unit	Test Method
Density	0.935	g/cm³	ASTM D1505
Apparent Density	0.46	g/cm³	ASTM D1895
Water Absorption (23°C, 24 hr)	< 0.010	%	ASTM D570
Average Molecular Weight	3.40E+6		Internal method
Average Particle Size	160	µm	Internal method

Mechanical	Nominal Value	Unit	Test Method
Taber Abrasion Resistance		mm³	ASTM D1044

Additional Information	Nominal Value	Unit	Test Method
Dynstat Impact	76.0	kJ/m²	Internal method
Sand Abrasion Wear - 1600rpm, 3h	3.0	mg	Internal method

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	40		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	41.0	MPa	ASTM D638
Tensile Elongation (Break)	350	%	ASTM D638
Flexural Modulus	590	MPa	ASTM D790
Coefficient of Friction	0.20		ASTM D1894

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	80.0	kJ/m²	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	75.0	°C	ASTM D648
Peak Melting Temperature	136	°C	ASTM D3418
CLTE - Flow	1.5E-6	cm/cm/°C	ASTM D696
Thermal Conductivity	0.40	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+17 - 1.0E+18	ohms·cm	ASTM D257
Dielectric Strength	50	kV/mm	ASTM D149
Dielectric Constant	2.30		ASTM D150
Dissipation Factor	2.0E-4 - 3.0E-4		ASTM D150

Resin Grade	Manufacturer	Category	Trademark
Razalen® P121 GR30	Razin™ Engineering Plastics	PP Impact Copolymer	Razalen®
Ravamid® BGF20 BK 45	Ravago Group	Nylon 6	Ravamid®
Elastron® TPO T401.D32.N	Elastron USA, Inc.	TPO (POE)	Elastron® TPO
Karina BLACK PVC COMPOUND 853-48/ 1-D-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
3M™ Dyneon™ Fluoroelastomer FE 5522	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer