Grilon® ELX 40 HNZ
| Category: | Nylon 6X , Polyamide 6X |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | es31Zw_Grilon-ELX-40-HNZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilon® ELX 40 HNZ is a Polyamide 6X (Nylon 6X) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for blow molding or extrusion. Important attributes of Grilon® ELX 40 HNZ are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.03 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.70 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 58 | 50 | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 550 | 250 | MPa | ISO 527-2 |
| Tensile Stress (50% Strain) | 21.0 | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 25 | 25 | kJ/m² | |
| 23°C | No Break | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 100 to 120 | -- | °C | |
| -- 2 | 180 | -- | °C | |
| Melting Temperature 3 | 210 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.6E-4 | -- | cm/cm/°C | |
| Transverse | 1.7E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 28 | 26 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA 6/X-HI, BGH, 32-005 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propak® 7021 | PolyPacific Pty. Ltd. | PP Homopolymer | Propak® |
| NuSil CV-2566 | NuSil Technology | Silicone | NuSil |
| Fluon® PTFE PA1020Z | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Enable™ 20-10 Series | ExxonMobil Chemical | mPE | Enable™ |
| Karina IVORY PVC COMPOUND 880-35/1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |