SABIC® Vestolen A 6013
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® Vestolen A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ergw1e_SABIC-Vestolen-A-6013.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®Vestolen A 6013 is a high-density polyethylene product,. It can be processed by extrusion, fiber (spinning) extrusion or injection molding, and is available in Europe. SABIC®The application fields of Vestolen A 6013 include textile/fiber, glue/gummed paper, hat/lid/bottle stopper, automobile industry and container. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, Compression Molded) | 63 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 55.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1280 | MPa | ISO 527-2/1BA/1 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 27.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 34.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 2000 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 525 | MPa | ISO 899-1 |
| 1000 hr | 275 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.8 | kJ/m² | ISO 180/1A |
| 23°C | 12 | kJ/m² | ISO 180/1A |
| Tensile Impact Strength | 49.0 | kJ/m² | ISO 8256/1B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 47.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 128 | °C | ISO 306/A50 |
| -- | 72.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| ESCR, SABIC Method, Compression Molded, Determined in Rhodacal-DS10 at 75°C, 3 N/mm², thickness 1mm: 85hrTensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 1.9%Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 34 MPaMelting Point, DIN 53765, Tmelt(top) at 5°C/min: 134°CEnthalpy Change, DIN 53765: 221J/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E590 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| REPOL® H080MA | Reliance Industries Limited | PP Homopolymer | REPOL® |
| UBESTA 3030 JI5L | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| DOW™ HDPE TCP-2495 NT | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Gallonprene® GP420-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |