EPO-TEK® 353ND-T4
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eqq2T6_EPO-TEK-353ND-T4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 353ND-T4 is a two component, highly thixotropic epoxy with non-flowing properties and high temperature resistance. This is a higher viscosity version of EPO-TEK® 353ND-T for applications needing decreased flow. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 409 | °C | TGA |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 225 | °C | |
| Intermittent | -55 to 325 | °C | |
| Storage Modulus (23°C) | 3.86 | GPa | |
| Thixotropic Index | 2.30 | ||
| Weight Loss on Heating | |||
| 200°C | 0.53 | % | |
| 250°C | 1.2 | % | |
| 300°C | 2.4 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 90.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.3E-5 | cm/cm/°C | |
| -- 3 | 2.3E-4 | cm/cm/°C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life 4 | 39 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | Tan | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.11 | g/cm³ | |
| Viscosity 7(23°C) | 11 to 17 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 180 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.21 | ||
| Volume Resistivity (23°C) | > 4.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 3.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Refrigerated |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-28160 | Teknor Apex Company | TPE | Monprene® |
| Vandar® 4632Z | Celanese Corporation | PBT | Vandar® |
| Greenflex® MQ 40 F | Versalis S.p.A. | EVA | Greenflex® |
| HAIPLEN H50 X2 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Paracril OZO® 733M60 | INSA | PVC+NBR | Paracril OZO® |