LNP™ STAT-KON™ AD000 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eotznm_LNP-STAT-KON-AD000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON AD000 is a compound based on ABS containing Carbon. Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound A- Product reorder name: AD000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.22 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.33 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2390 | MPa | ASTM D638 |
| -- | 2310 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 31.2 | MPa | ASTM D638 |
| Yield | 30.4 | MPa | ISO 527-2/5 |
| Break 3 | 29.1 | MPa | ASTM D638 |
| Break | 28.7 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 1.6 | % | ISO 527-2/5 |
| Break 5 | 6.5 | % | ASTM D638 |
| Break | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2480 | MPa | ASTM D790 |
| -- 7 | 2520 | MPa | ISO 178 |
| Flexural Strength 8(Break, 50.0 mm Span) | 59.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256 |
| 23°C 9 | 2.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D4812 |
| 23°C 10 | 23 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 94.3 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 94.5 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 80.1 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 80.2 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9218-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Network Polymers PP NPP 20-1202M | Network Polymers, Inc. | PP Random Copolymer | Network Polymers PP |
| BorSafe™ HE3495-LS-H | Borealis AG | HDPE | BorSafe™ |
| Desmopan® 786 S | Covestro - PUR | TPU, Unspecified | Desmopan® |
| Piolen® P XT11EMH102 | PiO Kunststoffe GmbH & Co KG | PP Copolymer | Piolen® P |