INSPIRE™ TF1501 ESU
| Category: | PP, Unspecified , Performance Polymers |
| Manufacturer: | Trinseo |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | emSrau_INSPIRE-TF1501-ESU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE™ TF1501 ESU has been developed for aesthetic automotive applications with good scratch resistance and UV light stabilisation. It is especially suitable for car interiors requiring ductility at ambient temperature. It combines low density, good stiffness and impact strength whilst maintaining excellent heat resistance and processability. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 1.4 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 50 | % | ISO 527-2/50 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Brittleness Temperature 1 | -10.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ISO 306/A120 |
| -- | 65.0 | °C | ISO 306/B50 |
| CLTE - Flow | ISO 11359-2 | ||
| -30 to 23°C | 6.5E-5 | cm/cm/°C | |
| 23 to 85°C | 1.0E-4 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2 mm |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen 2000HEXP | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| WPP PP WPP3208-FB BLK | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Andur AL 70 DP/Curene® 442 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Lucent PP GPP-130 | Lucent Polymers, Inc. | PP Homopolymer | Lucent PP |
| LNP™ LUBRICOMP™ HFG25Z compound | SABIC Innovative Plastics | Nylon 11 | LNP™ LUBRICOMP™ |