Order Products : sales@su-jiao.com
HiPrene® HT42
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | em2syB_HiPrene-HT42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® HT42 is a medium melt flow, 20% mineral filled polypropylene compound. This material is high stiffness and it is primarly designed for Home Appliance Parts but is suitable for other parts in automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 to 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1 | 9.0 to 15 | g/10 min | ISO 1133 |
| Ash Content (600°C) | 18 to 22 | % | ISO 3451-1A |
| Volatile Matter | 0.15 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 34.0 | MPa | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2/1A/50 |
| Flexural Modulus | 2700 | MPa | ISO 178/B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 30 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 140 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 799 X 112538 | RTP Company | HDPE | RTP |
| Taitacell EPS 301T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Alkathene® LD0128MS | Qenos Pty Ltd | LLDPE | Alkathene® |
| Kingfa PP-R2 | Kingfa | PP, Unspecified | Kingfa |
| HIPOL™ J700 | Mitsui Chemicals, Inc. | PP Homopolymer | HIPOL™ |