Mapex AN0720SB-02
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Mapex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | el5o8t_Mapex-AN0720SB-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mapex AN0720SB-02 is a 30% glass-fibre Reinforced nylon 6 heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (1.60 mm) | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr | 2.4 | % | ASTM D570 |
| 23°C, 24 hr | 2.4 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 147 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 9120 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 220 | °C | DSC |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 26 | kV/mm | ASTM D149, IEC 60243-1 |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength, ISO 180/1: 100 J/mArc Resistance, ASTM D495: 130 to 140 secDielectric Strength, ISO 243: 26 kV/mmThe value listed as Volume Resistance ICE 60093, was tested in accordance with IEC 167. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Nozzle Temperature | 240 - 250 | °C | |
| Mold Temperature | 30.0 - 100 | °C | |
| Injection Pressure | 50.0 - 120 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 30.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 0.300 | MPa | |
| Screw Speed | 60 - 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HKR102 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| SUPREME Specialty PS SP6432 9690 | Supreme Petrochem Ltd. | PS (MIPS) | SUPREME Specialty PS |
| TPX® RT31XB | Mitsui Chemicals, Inc. | PMP Copolymer | TPX® |
| Flontech® FT-905-ST | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Kazan LDPE 15313-003 OKP 22 1111 2002 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |