XYLEX™ X7519HP resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eiR8hR_XYLEX-X7519HP-resin-89337.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts may form opaque areas in the centre due to slow cooling. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.16 | % | |
| Equilibrium, 23°C, 50% RH | 0.14 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2470 | MPa | ASTM D638 |
| -- | 2370 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 58.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Break 3 | 66.0 | MPa | ASTM D638 |
| Break | 66.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 120 | % | ASTM D638 |
| Break | 130 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2240 | MPa | ASTM D790 |
| -- 7 | 2030 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 74.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 112 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 132 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 100 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Hopper Temperature | 50.0 | °C | |
| Rear Temperature | 275 to 285 | °C | |
| Middle Temperature | 280 to 290 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 65.0 to 75.0 | °C | |
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F737-BTB-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| YUPLENE® B920G | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| DELPET™ PM120N | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| Hy-Vin® VX332/1 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| Sylvin 4225-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |