Kepital® FL2005
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | KEP Americas |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | egyGF5_KepitalFL2005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 5% PTFE powder filled grade, good for general injection molding. FL2005 is suitable for parts that are required of low wear and friction. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| shrinkage- Flow 1(3.00 mm) | 2.0 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 58.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.5 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2550 | MPa | ISO 178 |
| Flexural Stress (23°C) | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 165 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 100mm diameter |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Therma-Tech™ TT6600-5001 EC Grey | PolyOne Corporation | Nylon 66 | Therma-Tech™ |
| COSMOPLENE® AS164 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| FHR Polypropylene P4G3Z-039 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| DuraFlex 717 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| Lupox® TE5000SZ | LG Chem Ltd. | PC+PBT | Lupox® |