barex® 210 Extrusion Grade
| Category: | Nitrile Resin , Acrylonitrile Copolymer |
| Manufacturer: | INEOS Barex |
| Trademark: | barex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | egM0dR_barex-210-Extrusion-Grade.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Barex 210 Extrusion Grade resin is an impact modified acrylonitrile-methyl acrylate copolymer with excellent gas barrier and a wide range of chemical resistance properties. It can easily be used for producing high barrier packaging by film and sheet extrusion, thermoforming, and extrusion blow molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 3380 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 96.5 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (23°C, 100% RH) | 0.31 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate | 2.0 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 76.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.9 | °C | ASTM D648 |
| CLTE - Flow (20 to 80°C) | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat (20°C) | 1340 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 254 µm) | 120 | ASTM D2457 | |
| Transmittance (254 µm) | 92.5 | % | ASTM D1003 |
| Haze (254 µm) | 2.7 | % | ASTM D1003 |
| Yellowness Index (0.254 mm) | 2.5 | YI | ASTM D1925 |
| Additional Information |
|---|
| Yield: 24080 in²-mil/lbMelt Index, ASTM D1238, 200°C/27.5 lbs: 3 g/10minWater Vapor Trans Rate, ASTM F1249-90, 100°F, 90% RH: 5 g-mil/100in²/24hrs-atmNitrogen Permeability, ASTM D3985, 73°F, 100% RH: 0.2 cm³-mil/100in²-24hrs-atmCarbon Dioxide Permeability, ASTM D3985, 73°F, 100% RH: 1.2 cm³-mil/100in²-24hrs-atm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 T-70A UV | RTP Company | TPU-Polyether | RTP |
| Staramide 6 80E7 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| LUVOCOM® 1/XCF/30 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Sylvin 9600-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP525N | LyondellBasell Industries | PP Homopolymer | Moplen |