| Prime ABS, High Impact, Natural |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.7 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 41.4 | MPa | ASTM D638 |
| Fracture | 31.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.1 | % | ASTM D638 |
| Fracture | 26 | % | ASTM D638 |
| Flexural Modulus (50.0 mm Span) | 2140 | MPa | ASTM D790 |
| Flexural Strength (Yield, 50.0 mm Span) | 68.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 370 | J/m | ASTM D256 |
| Instrumented Dart Impact | 31.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 97.2 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 82.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 - 93 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 188 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 216 - 238 | °C | |
| Nozzle Temperature | 218 - 260 | °C | |
| Mold Temperature | 49 - 71 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD DS201 | Pooya Polymer Tehran | Polyolefin, Unspecified | POYAD |
| tefabloc® TO 113 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| DOWLEX™ 4056.01G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| INSTRUC PPSLGF10 | Infinity LTL Engineered Compounds | PPS | INSTRUC |
| LEXAN™ R9453 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |