OmniLon™ PA6 U IM8 BK1000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ebgYZG_OmniLon-PA6-U-IM8-BK1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Impact, Utility Grade, Nylon 6 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2350 | MPa | ASTM D790 |
| Flexural Strength | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -34°C | 2.5 | kJ/m² | |
| -5°C | 6.3 | kJ/m² | |
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 60.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 238 to 282 | °C | |
| Middle Temperature | 249 to 293 | °C | |
| Front Temperature | 249 to 293 | °C | |
| Nozzle Temperature | 260 to 293 | °C | |
| Processing (Melt) Temp | 249 to 293 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1718-FP HO | LyondellBasell Industries | Polyolefin, Unspecified | SEQUEL® |
| XYRON™ TT520 | Asahi Kasei Chemicals Corporation | PPE+PP | XYRON™ |
| Andur 74-AGP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Flextuff® 2685 | Noble Polymers | TPE | Flextuff® |
| Hostacom ERC 198N G81493 | LyondellBasell Industries | PP Copolymer | Hostacom |