DIC.PPS Z-230
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ebFLPA_DIC-PPS-Z-230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9300 | MPa | ASTM D638 |
| Tensile Strength | 155 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | 8500 | MPa | ASTM D790 |
| Flexural Strength | 220 | MPa | ASTM D790 |
| Compressive Strength | 150 | MPa | ASTM D695 |
| Poisson's Ratio | 0.36 | ||
| Flexural Elongation at Break | 3.2 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Unnotched Izod Impact | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 100°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -30 to 100°C | 2.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 290 to 320 | °C | |
| Middle Temperature | 290 to 320 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V515TL40 | Lucent Polymers, Inc. | PP, Unspecified | Primefin |
| Sylvin 8865-75FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nycast 612VS C-80 | Cast Nylons Ltd. | Nylon 612 | Nycast |
| Excelprene® GE-9538L | S&E Specialty Polymers, LLC | PVC, Unspecified | Excelprene® |
| Hostacom ERC 161N C12380 | LyondellBasell Industries | PP Copolymer | Hostacom |