Greenflex® FC 45 F
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eZlNB2_Greenflex-FC-45-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex FC 45 F is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced by Greenflex FC 45 F exhibit good optical properties, excellent impact resistance and low creep. The resin shows outstanding bubble stability. Main Application Greenflex FC 45 F is recommended for the production of very wide agricultural films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 14.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 92 | ||
| Shore D, Injection Molded | 40 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 200 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 65.0 | MPa | |
| 1% Secant, TD : Blown Film | 70.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 5.00 | MPa | |
| TD : Yield, Blown Film | 4.00 | MPa | |
| MD : Break, Blown Film | 30.0 | MPa | |
| TD : Break, Blown Film | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 490 | % | |
| TD : Break, Blown Film | 650 | % | |
| Dart Drop Impact 1(Blown Film) | > 700 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 24.0 | kN/m | |
| TD | 40.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 73.0 | °C | ISO 306/A |
| Melting Temperature | 93.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 73 | ASTM D2457 | |
| Haze (Blown Film) | 4.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A MV 14 | A. Schulman Europe | PBT | SCHULADUR® |
| Sinvicomp SFE5529 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Wondel® B BH0 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| Ultramid® 8270 HS | BASF Corporation | Nylon 6 | Ultramid® |
| LUVOCOM® 1301-7578 VP | Lehmann & Voss & Co. | PPS | LUVOCOM® |