| Message |
|---|
| Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 10 | g/10 min | |
| 210°C/5.0 kg | 17 | g/10 min | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.48 | % | |
| Across Flow : 24 hr | 0.33 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break 2 | 5.00 | MPa | ASTM D638 |
| Break | 4.00 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 3 | > 400 | % | ASTM D638 |
| Break | > 400 | % | ISO 527-2/50 |
| Flexural Modulus 4 | |||
| 100 mm Span | 50.0 | MPa | ASTM D790 |
| -- | 50.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 46.0 | N/mm | ISO 6383-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -40.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.7E+16 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm, in Oil) | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.40 | ||
| 60 Hz | 2.40 | ||
| 1 MHz | 2.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.037 | ||
| 60 Hz | 0.037 | ||
| 1 MHz | 5.2E-4 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 210 to 240 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Nozzle Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Vent Depth | 0.030 to 0.050 | mm |
| Note Message | |
|---|---|
| 1 . | Results measured at 48 hrs |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2700 S-50A MD NATURAL | RTP Company | SEBS | RTP |
| Mirakutoran® TPU E490 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| EXCELLOY CW50 | Techno Polymer Co, Ltd. | AES+PC | EXCELLOY |
| DOWLEX™ 2006G | The Dow Chemical Company | HDPE | DOWLEX™ |
| Sylvin 5134-70 CLEAR RED 6153 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |