Plaslube® PC GF20 TL10 BK
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eY61H2_Plaslube-PC-GF20-TL10-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®PC GF20 TL10 BK is a polycarbonate (PC) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 101 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5860 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.23 | ASTM D1894 | |
| With steel-static | 0.21 | ASTM D1894 | |
| Wear Factor | 71 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.05 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 302 - 316 | °C | |
| Middle Temperature | 316 - 332 | °C | |
| Front Temperature | 310 - 327 | °C | |
| Nozzle Temperature | 310 - 327 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| HiFill® PA6 GF33 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Leona™ CR301 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Loyblend® YA-1002 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS+PBT | Loyblend® |
| SABIC® PPcompound 1961 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| apigo bio® CM 680 | API SpA | TPO (POE) | apigo bio® |