Stylac™ NF920
| Category: | ACS , Acrylonitrile Chlorinated Polyethylene Styrene |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Stylac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eXThok_Stylac-NF920.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stylac™ NF920 is an Acrylonitrile Chlorinated Polyethylene Styrene (ACS) product. It is available in Africa & Middle East, Asia Pacific, or Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 59 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 54.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 44.1 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2550 | MPa | ISO 178 |
| Flexural Stress 2 | 69.8 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.6 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 74.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 88.0 | °C | ISO 306/B |
| CLTE - Flow | 7.0E-5 to 1.0E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Ball Pressure Test | 80 | °C | EMAC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VA |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE HC1828 | Braskem | LLDPE | Braskem PE |
| Fainplast PVC MPH 95 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hyundai EP PPF HT315 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| POCAN® B 3217 XF 000000 | LANXESS GmbH | PBT | POCAN® |
| LNP™ THERMOCOMP™ QF008 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |