ENGAGE™ 8150
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eVgmUa_ENGAGE-8150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8150 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE) and is widely used in TPO applications where excellent low temperature impact properties are desired. ENGAGE 8150 provides high filler loading capability and outstanding peroxide cure capability. When cross-linked by peroxide, silane, or irradiation, it gives exceptional heat aging, compression set, and weather resistance properties and may be used to produce high performance electrical insulation. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.868 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 33 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 70 | ||
| Shore D, 1 sec, Compression Molded | 20 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 2.60 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 9.50 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 810 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 15.2 | MPa | |
| 2% Secant : Compression Molded | 14.4 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 37.3 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.0 | °C | Internal Method |
| Vicat Softening Temperature | 46.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 55.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 42.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPELIN® 6300B | MOL Petrochemicals Co. Ltd. | HDPE | TIPELIN® |
| DOW™ HDPE DGDB-5004 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| EPLAMID 6 GFR 5 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| ADVANCENE™ EE-1801-BSB | ETHYDCO | LLDPE | ADVANCENE™ |
| NORYL™ GFN1F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |