FERREX® GPP35CS33UL-BK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eVaRgz_FERREX-GPP35CS33UL-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERREX® GPP35CS33UL-BK is a Polypropylene material filled with 36% calcium carbonate. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of FERREX® GPP35CS33UL-BK are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | |
| Across Flow | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 19.3 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 150 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 1480 | MPa | |
| Tangent : 23°C | 1660 | MPa | |
| Flexural Strength (23°C) | 33.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 610 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Gardner Impact (23°C, 3.18 mm) | 18.6 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 96.1 | °C | |
| 1.8 MPa, Unannealed | 54.4 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 199 to 204 | °C | |
| Middle Temperature | 204 to 210 | °C | |
| Front Temperature | 210 to 216 | °C | |
| Nozzle Temperature | 216 to 221 | °C | |
| Mold Temperature | 46.1 to 60.0 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACRYLITE® Satinice df22 8N | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| Compoceran E103D | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| EPO-TEK® OE184 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Piolen® P T30LA47 | PiO Kunststoffe GmbH & Co KG | PP Copolymer | Piolen® P |
| KMI PP KM061-JC | KMI Group, Inc. | PP Homopolymer | KMI PP |