RheTech Polypropylene M30P100-01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eUqgGQ_RheTech-Polypropylene-M30P100-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Mica Reinforced, Polypropylene, Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 29.4 | MPa | ASTM D638 |
| Flexural Modulus | 3720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Dart Drop Impact | 0.452 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 127 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 204 - 232 | °C | |
| Middle Temperature | 210 - 238 | °C | |
| Front Temperature | 216 - 243 | °C | |
| Nozzle Temperature | 232 - 277 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adflex Z 101 H | LyondellBasell Industries | TPO (POE) | Adflex |
| Compoceran E102 | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| Flontech® FT-BRR25-CF10-M5-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Ecotan B F50 FL NERO | Soredi S.p.a. | Nylon 6 | Ecotan B |
| Karina GRAY PVC COMPOUND 802-18/462-C-ERB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |