Generic PPSU
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eUQK7e_Generic-PPSU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPSU This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.28 - 1.36 | g/cm³ | ASTM D792 |
| 23°C | 1.29 - 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (365°C/5.0 kg) | 7.0 - 37 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.70 - 0.71 | % | ASTM D955 |
| 23°C | 0.70 - 1.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.36 - 0.38 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2330 - 2360 | MPa | ASTM D638 |
| 23°C | 2270 - 2800 | MPa | ISO 527-2 |
| Tensile Strength (23°C) | 69.1 - 70.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 7.0 - 90 | % | ASTM D638 |
| Fracture, 23°C | 28 - 90 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2340 - 2410 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 89.3 - 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 680 - 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 206 - 209 | °C | ASTM D648 |
| CLTE - Flow | |||
| -- | 5.5E-5 - 7.2E-5 | cm/cm/°C | ASTM D696 |
| -- | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+12 - 9.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 12 - 200 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 3.32 - 3.54 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 180 | °C | |
| Drying Time | 2.5 - 6.0 | hr | |
| Rear Temperature | 350 - 374 | °C | |
| Middle Temperature | 360 - 385 | °C | |
| Front Temperature | 374 - 395 | °C | |
| Nozzle Temperature | 368 - 370 | °C | |
| Processing (Melt) Temp | 360 - 390 | °C | |
| Mold Temperature | 135 - 160 | °C | |
| Injection Pressure | 86.2 - 103 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPSUThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-75A | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| SCHULAMID® 612 GF 30 H9 | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Unichem 8060 | Colorite Polymers | PVC, Flexible | Unichem |
| NOVADURAN® 5010GT15 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| ExxonMobil™ LDPE LD 306 Series | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |