EMPILON® 8879

Category:	SEBS , Styrene Ethylene Butylene Styrene Block Copolymer
Manufacturer:	EMPILON
Trademark:	EMPILON®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eTnDb4_EMPILON-8879.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Comply with WEEE/RoHS directive

Comply with SONY SS-00259 6th requirement

Free of Phthalates plasticizer

Non-toxic and free of TetraBisPhenol A

UL 94 V-0 flame class rating (UL File No.E196953)

EMPILON® 8800 series compound has excellent mechanical properties, good electrical property, low specific gravity and unique anti-flame ability without PBB and PBDE retardants, and are wildly applied to wire & cable, plug and flat cable for commu- nication applications. Hydrogenated Styrenic Block Copolymer is the main content of this 8800 series compound, its hardness range is from Shore A 65 to 95 and can be processed by ordinary plastic machinery for Injection, extrusion or calendaring etc.

EMPILON® 8800 series products are 100% recyclable and retain good mechanical properties after heat, weathering and solvent resistance testing and won't hydrolyze in water. They need 80~90°C dehumidified hot air at least 2 hours before any molding process and need to be continually dried during operation. For coloring, please select color master batch based on PE or EVA material with the exception of PVC, non-blooming black color compound is available. Higher screw speed and backpressure are needed for better colorant dispersion.

General Information
Features	Block Copolymer Low density Recyclable materials Good electrical performance Hydrolysis resistance Non-toxic
Uses	Wire and cable applications Communication application
RoHS Compliance	RoHS compliance
UL File Number	E196953
Forms	Particle
Processing Method	Extrusion Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.28	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	13	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	86		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength	10.0	MPa	ASTM D412
Tensile Elongation (Break)	600	%	ASTM D412

Thermal	Nominal Value	Unit
Brittleness Temperature	-45.0	°C

Flammability	Nominal Value		Test Method
Flame Rating	V-0		UL 94

Additional Information	Nominal Value	Unit	Test Method
Breakdown Voltage	20000	V	ASTM D149

Extrusion	Nominal Value	Unit
Extruder Screw L/D Ratio	> 24.0
Extruder Screw Compression Ratio	2.40 - 3.50

Injection	Nominal Value	Unit
Drying Temperature	80.0 - 90.0	°C
Drying Time	2.0	hr
Rear Temperature	165 - 185	°C
Middle Temperature	190 - 210	°C
Front Temperature	190 - 210	°C
Nozzle Temperature	190 - 210	°C
Processing (Melt) Temp	190 - 220	°C
Mold Temperature	40.0 - 60.0	°C
Injection Pressure	2.94 - 4.90	MPa
Injection Rate	Moderate-Fast
Back Pressure	0.785 - 1.18	MPa
Screw L/D Ratio	20.0:1.0

Injection instructions
Hold Time: 5 sec.

Extrusion	Nominal Value	Unit
Drying Temperature	80.0 - 90.0	°C
Drying Time	2.0	hr
Cylinder Zone 1 Temp.	190 - 200	°C
Cylinder Zone 2 Temp.	195 - 210	°C
Cylinder Zone 3 Temp.	200 - 215	°C
Cylinder Zone 4 Temp.	190 - 210	°C
Cylinder Zone 5 Temp.	190 - 210	°C
Melt Temperature	190 - 220	°C
Die Temperature	190 - 210	°C

Extrusion instructions
Screen Pack: 80/100Conductor pre-heat temperature: 110-150°C

Resin Grade	Manufacturer	Category	Trademark
WPP PP PPC6TF2UV-Black	Washington Penn Plastic Co. Inc.	PP Copolymer	WPP PP
4PROP® 5C10800	4Plas	PP Copolymer	4PROP®
APEX® 3611-95	Teknor Apex Company	PVC, Flexible	APEX®
Globalene® 6331	Lee Chang Yung Chemical Industry Corp.	PP Homopolymer	Globalene®
Maxxam™ PP5120F B2	PolyOne Corporation	PP Homopolymer	Maxxam™