CERTENE™ HI-452
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eTIpEH_CERTENE-HI-452.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HI-452 is a certified prime copolymer designed for molding industrial applications requiring excellent toughness and moderate stiffness. HI-452 features easy processability, superior Environmental Stress Cracking Resistance (ESCR), excellent impact strength, good dimensional stability and warpage resistance. HI-452 suggested applications include industrial containers and lids, 1 to 5 gallon pails, tote boxes, housewares, toys and structural foam. HI-452 recommended processing temperature is 230 to 270°C. with mold @ 20 to 40°C. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, Compression Molded, F50) | 16.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 1000 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Compression Molded) | 1170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 73.6 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 76.0 | °C | ASTM D648 |
| Brittleness Temperature | -90.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® PPS GF30 TS0 | EPIC Polymers | PPS | TRIBOCOMP® |
| Geon™ Vinyl Flexible R7661A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Petroquim PP PH 0362 | Petroquim S.A. | PP Homopolymer | Petroquim PP |
| Hostacom M4 U42 LW92607 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LNP™ LUBRICOMP™ KL004 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |