| TRIBOCOMP®PEEK CF30 TS0 is a polyetheretherketone (PEEK) product, which contains 15% ptfe fiber and 20% carbon fiber reinforced materials. It is available in Europe. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 17500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 15500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 250 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.19 | ASTM D3702 | |
| Static | 0.18 | ASTM D3702 | |
| Wear Factor | 15.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 320 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 315 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 1.5E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.60 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 340 - 360 | °C | |
| Middle Temperature | 360 - 380 | °C | |
| Front Temperature | 380 - 390 | °C | |
| Nozzle Temperature | 380 - 390 | °C | |
| Mold Temperature | 160 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HI5303R | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TATREN® IM 6 56 | Slovnaft Petrochemicals, s.r.o. | PP Impact Copolymer | TATREN® |
| CALFIN 1152CF | Pooya Polymer Tehran | Polyolefin, Unspecified | CALFIN |
| Celanex® 2008 | Celanese Corporation | PBT | Celanex® |
| Hanwha Total PP FH43 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |