CELEX™ 5200HF.IM
| Category: | PC+ABS , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CELEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eT0Qx6_CELEX-5200HF-IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CELEX 5200HF.IM advanced resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. Its superior processing makes it ideal for molding large parts and optimizing cycle time productivity in injection molding operations. This resin is suitable for use in a wide variety of applications in the information technology equipment and consumer electronics markets. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 17 | g/10 min | |
| 260°C/5.0 kg | 75 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded 1 | 62.1 | MPa | |
| Break, 3.20 mm, Injection Molded | 46.2 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 4.0 | % | |
| Break, 3.20 mm, Injection Molded | 50 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2830 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 97.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm, Injection Molded | 93.9 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm, Injection Molded | 82.2 | °C | |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3(1.50 mm) | V-0 | UL 94 | |
| Oxygen Index 4 | 29 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 to 90.6 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 60.0 to 90.6 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Metton® LMR M15XX | Metton America, Inc. | DCPD | Metton® LMR |
| XYRON™ X531Z | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| EverGlide® SG3264 | Polymer Dynamix | PEEK | EverGlide® |
| EPO-TEK® T7109-17 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| 3M™ Dyneon™ Fluoroelastomer FC 2179 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |