Order Products : sales@su-jiao.com

KPOL-PP K-PPH 3.5

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eSz5Oh_KPOL-PP-K-PPH-3-5.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Homopolymer

Applications

The KPOL® is a medium fluidity homopolymer used for general purpose and multipurpose grade for extrusion and injection moulding applications.

Flip-top and resealable closures, thick wall parts, domestic appliances, industrial bags and big bags, compounds, curtains and covers to aviary and agriculture, monofilament for ropes, fishing nets, cables for boats, bristles for tooth brushes and brooms.

Characteristics

The KPOL® is specially developed for Production of Raffia (Flat Yarn) by Flat Die Extrusion (Water Quenched or Chill Roll), Injection Molding of thick parts, caps, closures, etc.

This product exhibits excellent processability, good melt stability, good stiffness/impact strength balance and low odor and flavor transfer. It is a controlled rheology grade.

General Information
Additive	Antioxidant Processing Aid
Features	Antioxidant Controlled Rheology Food Contact Acceptable Good Impact Resistance Good Processability Good Stiffness High Melt Stability Homopolymer Low Odor Transfer Low Taste Transfer Medium Flow
Uses	Agricultural Applications Appliances Bags Caps Closures Compounding General Purpose Monofilaments Netting Rope Thick-walled Parts Yarn
Agency Ratings	FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	3.5	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	73		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, Compression Molded)	36.0	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	9.0	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	1550	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	45	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded)	91.0	°C	ASTM D648
Vicat Softening Temperature	155	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Ultramid® A3K BK00464	BASF Corporation	Nylon 66	Ultramid®
4MID® 9B32330	4Plas	Nylon 6	4MID®
Akulon® K225-KV	DSM Engineering Plastics	Nylon 6	Akulon®
APEX® 86-K264A-NT	Teknor Apex Company	PVC, Flexible	APEX®
Leona™ 53G33	Asahi Kasei Chemicals Corporation	Nylon 66	Leona™