LNP™ COLORCOMP™ J1000Z-WH9G618 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eSstkZ_LNP-COLORCOMP-J1000Z-WH9G618-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* COLORCOMP* J1000-WH9G618 is a compound based on Polyethersulfone resin. Added Features include; Extrusion Grade, Customer specific color. Also known as: LNP* COLORCOMP* Compound J1000Z-WH9G618 Product reorder name: J1000Z-WH9G618 |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2800 | MPa | ISO 178 |
| Flexural Stress | 131 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.8E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA610 A6G6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 610 | Shandong PA610 |
| VAMPTER 3026 V0 | Vamp Tech | PBT | VAMPTER |
| Ablefilm 550 | Henkel Ablestik | Epoxy | Ablefilm |
| Gallonprene® GP520-8502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LTP ZC-3160A | Chengdu Letian Plastics Co., Ltd | PPS Alloy | LTP |