LNP™ VERTON™ EV008 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eSl5oV_LNP-VERTON-EV008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON EV008 is a compound based on Polyetherimide containing 40% Long Glass Fiber. Added feature of this grade is: Structural. Also known as: LNP* VERTON* Compound EXVT0010 Product reorder name: EV008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 15100 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 187 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 14400 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 268 | MPa | ASTM D790 |
| Compressive Strength | 282 | MPa | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 20 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 42 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 206 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 343 to 360 | °C | |
| Middle Temperature | 350 to 362 | °C | |
| Front Temperature | 350 to 362 | °C | |
| Processing (Melt) Temp | 350 to 362 | °C | |
| Mold Temperature | 148 to 162 | °C | |
| Back Pressure | 0.290 to 0.430 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULABLEND® (ABS/PA) M/MK 20 GF | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |
| Baydur® 726 IBS (40 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Kingfa PA66-RG201 | Kingfa | Nylon 66 | Kingfa |
| INLUBE PEEKCF20TF15 | Infinity LTL Engineered Compounds | PEEK | INLUBE |
| Sylvin 3200-65 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |