Skyrol® SP19N
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eRZLfF_Skyrol-SP19N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SP19N is a heat-shrinkable polyester film with relatively high shrinking characteristics. It is applicable in various shrinkable packaging, such as outer wrapping for PET and glass bottles, cans and other kinds of containers. One side of SP19N is anti-static treated for better processibility. It can be used as an alternative material for PVC. This is applicable to hot air also. SP19N is currently available in 160 and 200 gauges. Other gauges may be available on special request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.32 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow 2 | Internal Method | ||
| 100°C, 0.0400 mm | 2.1 | % | |
| 100°C, 0.0500 mm | 2.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 3 | 0.30 | ||
| vs. Itself - Dynamic 4 | 0.30 | ||
| vs. Itself - Static 5 | 0.40 | ||
| vs. Itself - Static 6 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm | 62.1 | MPa | |
| MD : Yield, 50 µm | 62.1 | MPa | |
| TD : Yield, 40 µm | 248 | MPa | |
| TD : Yield, 50 µm | 248 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm | 560 | % | |
| MD : Break, 50 µm | 570 | % | |
| TD : Break, 40 µm | 84 | % | |
| TD : Break, 50 µm | 87 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 40.0 µm | 193 | ||
| 50.0 µm | 149 | ||
| Haze | ASTM D1003 | ||
| 40.0 µm | 4.0 | % | |
| 50.0 µm | 3.9 | % |
| Note Message | |
|---|---|
| 1 . | 50 µm |
| 2 . | 10 sec water bath |
| 3 . | 50 µm |
| 4 . | 40 µm |
| 5 . | 40 µm |
| 6 . | 50 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 124N/L | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| WPP TPO TPO-257 | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| HiFill® PA6/6 GF/M25 HS L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| LNP™ THERMOCOMP™ QC006 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| OTECH PVC OW134 - Automotive Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |