TRIEL® 5722EM
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eQbfV8_TRIEL-5722EM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIEL® 5722EM is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.7 to 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 41.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 400 | % | ASTM D638 |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 36.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -40°C | 98 to 130 | J/m | |
| 23°C | 200 to 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 128 | °C | ASTM D648 |
| Vicat Softening Temperature | 205 | °C | ASTM D1525 1 |
| Melting Temperature | 216 | °C | ASTM D2117 |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CERTENE™ HR-242U | Muehlstein | HDPE | CERTENE™ |
| Fainplast PVC PHS 75/B | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Lupox® SG3250 | LG Chem Ltd. | PBT | Lupox® |
| OnFlex™ S HF 60A-3S1982 | PolyOne Corporation | TPE | OnFlex™ |
| LUVOCOM® 3-9064 | LEHVOSS Group | Nylon 6 | LUVOCOM® |