LEXAN™ 123M resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ePTrpG_LEXAN123Mresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nonhalogenated. 17.5 MFR, for small, intricate parts. UV stabilized. Improved Internal mold release. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ASTM D792 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Equilibrium, 100°C | 0.58 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 63.0 | MPa | ASTM D638 |
| Fracture | 66.0 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 120 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 200 | J/m | ASTM D256 |
| 23°C | 820 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 77.0 | J | ASTM D3763 |
| Dart Drop Impact (23°C) | 169 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 132 | °C | ASTM D648 |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 5 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1260 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 260 - 282 | °C | |
| Middle Temperature | 271 - 293 | °C | |
| Front Temperature | 282 - 304 | °C | |
| Nozzle Temperature | 277 - 299 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 71 - 93 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 100 FR | RTP Company | PP, Unspecified | RTP |
| VITAMIDE® BI12BK9012 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| KOCETAL® UR304BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| LubX® C extr. | Röchling Engineering Plastics SE & Co. KG | UHMWPE | LubX® |
| TechnoPet GF 45 2 1 | TechnoCompound GmbH | PET | TechnoPet |