ASTALAC™ ABS GSM
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eNxRAd_ASTALAC-ABS-GSM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS GSM is a high impact strength grade of ABS and is designed for injection moulding applications requiring superior toughness and abuse resistance whilst maintaining a balance of product rigidity, heat resistance and mouldability. Typical automotive applications include painted front grilles and decor panels, other areas of use include vacuum cleaner nozzles and pool filtration equipment. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ GSM-UV ]. Underwriters Laboratory Reference E183535-B. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 14 | g/10 min | |
| 230°C/3.8 kg | 3.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2250 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 330 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 25.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 77.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 83.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 88.0 | °C | |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 205 to 225 | °C | |
| Middle Temperature | 215 to 235 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4200 TFE 20 | RTP Company | PI, TP | RTP |
| Miramid® SE30C | BASF Leuna GmbH | Nylon 66 | Miramid® |
| SAXAMID™ 226F6RY01 | SAX Polymers | Nylon 66 | SAXAMID™ |
| LG ABS XR409E | LG Chem Ltd. | ABS | LG ABS |
| Braskem PE GP100BLXP | Braskem | HDPE | Braskem PE |