Order Products : sales@su-jiao.com
Innothane® IE-3075
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eMgsQi_Innothane-IE-3075.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-3075 is a rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.11 | g/cm³ | |
| Hardener | 1.11 | g/cm³ | |
| Base Resin | 1.25 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Compressive Modulus | 2070 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 83.0 | °C | |
| 1.8 MPa, Unannealed | 81.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 89 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 30 to 90 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.075 | Pa·s | |
| 25°C 2 | 0.30 | Pa·s | |
| 25°C 3 | 0.85 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 6.0 to 10 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation at Break | 9.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 200°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551400-100 (4.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Moplen HP2981 | LyondellBasell Industries | PP Homopolymer | Moplen |
| Edgetek™ CY1000 UV NHFR V0 GR723 | PolyOne Corporation | PC+ABS | Edgetek™ |
| LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| TABOREN® PH 49 G 30-045 | SILON s.r.o. | PP Homopolymer | TABOREN® |