LUVOCOM® 1301-0915 Datasheet,PPS,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1301-0915 is a linear polyphenylene sulfide material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1301-0915 are: Flame Retardant Conductivity High stiffness high strength Electrostatic protection Typical application areas include: textile/fiber engineering/industrial accessories Automotive Industry business/office supplies medical/health care

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Additive	PTFE lubricant
Features	Conductivity Low friction coefficient Rigidity, high High strength Electrostatic discharge protection Good creep resistance Good wear resistance Heat resistance, high Lubrication Flame retardancy
Uses	Textile applications Engineering accessories Application in Automobile Field Business equipment Medical/nursing supplies
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.49	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.50	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.050	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	13000	MPa	ISO 527-2
Tensile Stress (Break)	125	MPa	ISO 527-2
Tensile Strain (Yield)	1.2	%	ISO 527-2
Flexural Modulus	10000	MPa	ISO 178
Flexural Stress	175	MPa	ISO 178
Coefficient of Friction
Dynamic	0.20
Static	0.14
Flexural Strain at Flexural Strength	1.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	240	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	19	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	220	°C	ISO 75-2/A
Continuous Use Temperature	220	°C	UL 746B
CLTE - Flow	3.0E-5	cm/cm/°C	DIN 53752

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+3	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
B	50.0 - 90.0	°C
Hot air dryer, A	100 - 140	°C
Drying Time
B	> 4.0	hr
Hot air dryer, A	2.0 - 4.0	hr
Rear Temperature	300 - 320	°C
Middle Temperature	310 - 330	°C
Front Temperature	320 - 340	°C
Nozzle Temperature	320 - 340	°C
Processing (Melt) Temp	330	°C
Mold Temperature	150 - 180	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PPS , Polyphenylene Sulfide
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eMg9HT_LUVOCOM-1301-0915.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC 6930 013	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
WELLAMID Nylon 6600/50 GV 15 HWCP	CP-Polymer-Technik GmbH & Co. KG	Nylon 66	WELLAMID Nylon
LUCITE® Acritherm™ HS3125	Lucite International Inc.	Acrylic (PMMA)	LUCITE®
Integra™ PC-5022 R UV 0001	PolySource, LLC	PC	Integra™
VisiJet® FTX Silver	3D Systems	Unspecified	VisiJet®