Promyde® B15 P
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eMdFs0_Promyde-B15-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde® B15 P is a Polyamide 6 heat stabilised, nucleated and lubricated. CHARACTERISTICS Promyde B15 P is a polyamide 6 heat stabilized, lubricated and nucleated for fast cycle injection moulding. Its main characteristics are easy flowing, easy mould filling and very fast cooling time whilst maintaining excellent polyamide 6 mechanical properties. APPLICATIONS Due to its easy flow characteristics and very fast cooling time; Promyde B15 P provides significant productivity improvement. Promyde B15 P mould filling is 35 % faster than standard viscosity polyamide 6; that combined with its excellent mechanical and thermal properties make it suitable for high speed multi cavity injection moulding of small parts such as components used in automotive, electrical, electronics, or technical parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 260 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.80 - 1.1 | -- | % | ISO 294-4 |
| Flow direction | 0.90 - 1.1 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 9.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Viscosity Number | 120 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3300 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 85.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield, 23°C | 3.5 | 25 | % | ISO 527-2/50 |
| Fracture, 23°C | 18 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2800 | 1000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 110 | 30.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.5 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 320 | -- | kJ/m² | ISO 179/1eU |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 187 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 850 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.50 mm) | 700 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back Pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 310 | Wacker Chemie AG | Silicone | POWERSIL® |
| TEREZ PA 6.6 7750 T/1 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| ECP 125 | TBA Electro Conductive Products Ltd. | LDPE | ECP |
| LNP™ THERMOCOMP™ NF001 compound | SABIC Innovative Plastics | PC+ABS | LNP™ THERMOCOMP™ |
| LEXAN™ EXL5689 resin | SABIC Innovative Plastics | PC | LEXAN™ |