POTICON RBA514

Category:	PPS , Polyphenylene Sulfide
Manufacturer:	Otsuka Chemical Co., Ltd.
Trademark:	POTICON
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	eLuCix_POTICONRBA514.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs.

Advantages

Microscopic reinforcement

Superior friction sliding and wear reduction

Excellent dimensional accuracy and surface smoothness

Highly recyclable

Applications

Automotive Parts (gears, bearings)

LED Reflectors

Watch Parts (gears, ground plane)

Camera (image stabilization parts)

Sliding Parts (gears, wheel bearing)

Camera Module Parts

Motor Parts (cog-wheels, bearings)

RBA514 Property: Slide

General Information
Features	High Dimensional Stability Low friction coefficient Recyclable materials
Uses	LEDs Gear Application in Automobile Field Camera application Bearing
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.60	g/cm³	ASTM D792
Molding Shrinkage
Flow	0.60	%
Transverse flow	1.3	%
Water Absorption (Equilibrium)	0.020	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	75		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	78.0	MPa	ASTM D638
Tensile Elongation (Break)	2.2	%	ASTM D638
Flexural Modulus	7100	MPa	ASTM D790
Flexural Strength	120	MPa	ASTM D790
Coefficient of Friction (vs. Steel - Dynamic)	0.20
Abrasion Loss
-- ¹	2.00	10^-3 mm³/N·km
of counterpart ²	0.00	10^-3 mm³/N·km

Thermal	Nominal Value	Unit	Test Method
Heat Distortion	218	°C	ASTM D648

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	25	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	2.5E-5	cm/cm/°C	ASTM D696

Flammability	Nominal Value		Test Method
Flame Rating	V-0		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	290 - 320	°C
Mold Temperature	120 - 150	°C
Injection Pressure	70.0 - 100	MPa

Note Message
1 .	Surface pressure: 1MPa
2 .	Slipping velocity: 0.3m/sec

Resin Grade	Manufacturer	Category	Trademark
Telcar® TL-1444A	Teknor Apex Company	TPE	Telcar®
Alkatuff® 425	Qenos Pty Ltd	LLDPE	Alkatuff®
INSTRUC FEPGF10	Infinity LTL Engineered Compounds	FEP	INSTRUC
LNP™ THERMOCOMP™ OF008 compound	SABIC Innovative Plastics	PPS, Linear	LNP™ THERMOCOMP™
LNP™ LUBRILOY™ R2000A compound	SABIC Innovative Plastics	Nylon 66	LNP™ LUBRILOY™