Stanyl® TS200F6
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eLDdBt_Stanyl-TS200F6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stanyl® TS200F6 is a Polyamide 46 (Nylon 46) material filled with 30% glass fiber. It is available in Asia Pacific. Primary attribute of Stanyl® TS200F6: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 10000 | 6000 | MPa | |
| 120°C | 5500 | -- | MPa | |
| 160°C | 5000 | -- | MPa | |
| 180°C | 4400 | -- | MPa | |
| 200°C | 4000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 210 | 115 | MPa | |
| Break, 120°C | 110 | -- | MPa | |
| Break, 160°C | 100 | -- | MPa | |
| Break, 180°C | 95.0 | -- | MPa | |
| Break, 200°C | 90.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 4.0 | 7.0 | % | |
| Break, 120°C | 7.5 | -- | % | |
| Break, 160°C | 7.5 | -- | % | |
| Break, 180°C | 7.5 | -- | % | |
| Break, 200°C | 7.5 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 9000 | 5500 | MPa | |
| 120°C | 4700 | -- | MPa | |
| 160°C | 3900 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 12 | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 75 | kJ/m² | |
| 23°C | 80 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 11 | 11 | kJ/m² | |
| 23°C | 12 | 21 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C | |
| Thermal Index - 5000 hr | 152 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.830 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 TFE 20 SI 2 | RTP Company | Nylon 66 | RTP |
| PRL PEI-GP1-TFE5 | Polymer Resources Ltd. | PEI | PRL |
| Boltaron 9250 | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| Filter-bond™ R-37-38 | Hapco Inc. | TS, Unspecified | Filter-bond™ |
| Geon™ Vinyl Rigid Extrusion L0111 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |