Vitaster® UR34NT6222
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Vitaster® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eI5qmm_Vitaster-UR34NT6222.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vitaster® UR34NT6222 is a Polybutylene Terephthalate (PBT) product filled with 20% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 170 | MPa | ISO 178 |
| Break | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 220 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 225 | °C | ASTM D2117, ISO 1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 31 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1320 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| TPSiV™ 3345-65A NAT 25564 | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Cellophane™ 335PS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Huaxia Shenzhou DS608-A | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluoropolymer | Huaxia Shenzhou |
| Lucent PBT GPB-130L | Lucent Polymers, Inc. | PBT | Lucent PBT |