OPNYL OP66GF13
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eGsuhW_OPNYL-OP66GF13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 66 - Glass reinforced (13 %), high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.17 mm | 0.10 to 0.20 | % | |
| Across Flow : 3.17 mm | 1.0 to 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3900 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 100 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 5000 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 240 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 235 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G30V0BLS | Kolon Plastics, Inc. | PBT | SPESIN® |
| TRIREX® 3026B(R) | Samyang Corporation | PC | TRIREX® |
| DURACON® TR-20 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Lotrène® LDPE FD0270 | QAPCO | LDPE | Lotrène® LDPE |
| Kepital® F15-33 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |